Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere
Mathan, M. Bobby, Raja, V.S., and Mukhopadhyay, A.K. (2004) Determination of true stress corrosion cracking susceptibility index of a high strength Al alloy using glycerin as the non-corrosive atmosphere. Scripta Materialia, 51 (11). pp. 1075-1079.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://dx.doi.org/10.1016/j.scriptamat.2...
The purpose of this work is to show that during slow strain rate testing (SSRT), the laboratory air might not be a non-corrosive atmosphere for evaluating the Iscc (stress corrosion cracking susceptibility index) of high strength Al alloys. Instead, it is proposed that glycerin could be effectively used as the non-corrosive atmosphere to find out the correct Iscc. This is demonstrated while examining 7010 Al alloy in the under aged condition.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||7010 Al alloy; stress corrosion cracking index; slow strain rate testing|
|FoR Codes:||09 ENGINEERING > 0912 Materials Engineering > 091207 Metals and Alloy Materials @ 100%|
|SEO Codes:||86 MANUFACTURING > 8611 Basic Metal Products (incl. Smelting, Rolling, Drawing and Extruding) > 861101 Basic Aluminium Products @ 100%|
|Deposited On:||28 Apr 2010 09:22|
|Last Modified:||13 May 2013 01:08|
Last 12 Months: 0
|Citation Counts with External Providers:||Web of Science: 8|
Repository Staff Only: item control page