Biofilm formation on surface characterized micro-implants for skeletal anchorage in orthodontics
Chin, Mervyn Y.H., Sandham, Andrew, De Vries, Joop, van der Mei, Henny C., and Busscher, Henk J. (2007) Biofilm formation on surface characterized micro-implants for skeletal anchorage in orthodontics. Biomaterials, 28 (11). pp. 2032-2040.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://dx.doi.org/10.1016/j.biomaterials...
Micro-implants are increasingly popular in clinical orthodontics to effect skeletal anchorage. However, biofilm formation on their surfaces and subsequent infection of peri-implant tissues can result in either exfoliation or surgical removal of these devices. The present study aimed to assess biofilm formation on five commercially available, surface characterized micro-implant systems in vitro. The elemental surface compositions of as-received and autoclave-sterilized micro-implants were characterized by X-ray photoelectron spectroscopy. High carbon contamination was detected on the oxide surfaces, along with traces of inorganic elements (Ca, Cu, Cr, Pb, Zn, and P) which disappeared after Ar+ ion sputtering. The mean surface roughnesses (Ra) were around 182nm for titanium microimplants, and 69nm for stainless steel micro-implants, as measured by atomic force microscopy. Scanning electron microscopy revealed different surface topographies between manufacturers, varying from typical machined grooves to structural defects like pores and pits. Overnight biofilms were grown on micro-implant surfaces by immersion in pooled human whole saliva. Biofilms on micro-implants treated with chlorhexidine and fluoride mouthrinses contained comparable numbers of viable organisms, but significantly less than did untreated micro-implants. Comparison of different implant systems using multiple linear regression analysis indicated that biofilm formation was governed by roughness of the implant surface and the prevalence of carbon- and oxygen-rich components.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||biofilm; titanium; stainless steel; orthodontic micro-implants; Chlorhexidine; Fluoride|
|FoR Codes:||11 MEDICAL AND HEALTH SCIENCES > 1105 Dentistry > 110501 Dental Materials and Equipment @ 50%|
11 MEDICAL AND HEALTH SCIENCES > 1105 Dentistry > 110506 Orthodontics and Dentofacial Orthopaedics @ 50%
|SEO Codes:||92 HEALTH > 9201 Clinical Health (Organs, Diseases and Abnormal Conditions) > 920113 Oro-Dental Disorders @ 100%|
|Deposited On:||29 Mar 2010 11:13|
|Last Modified:||12 Feb 2011 23:43|
Last 12 Months: 0
Repository Staff Only: item control page