Critical zeta potential and the Hamaker Constant of oxides in water
Leong, Y.K., and Ong, B.C. (2003) Critical zeta potential and the Hamaker Constant of oxides in water. Powder Technology, 134 (3). pp. 249-254.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://dx.doi.org/10.1016/j.powtec.2003....
The critical zeta potential characterises the flocculated–dispersed state transition of a colloidal dispersion. For many colloidal dispersions, yield stress displayed a linear relationship with the square of zeta potential indicating that they obeyed the Derjaguin–Landau–Verwey–Overbeek (DLVO) theory. From this relationship, critical zeta potential is obtained from the intercept at the zeta potential axis at a yield stress of zero. The critical zeta potential is a measure of the repulsive potential required to exactly counter the maximum attractive potential between particles in dispersion in the flocculated state. When the forces of interaction between particles in the dispersion are only the van der Waals and electrostatic forces, then the critical zeta potential is indirectly a measure of the van der Waals attractive potential and, hence, it may be used to determine the Hamaker constant of solids in water. This potential is proportional to the square root of the solids Hamaker constant in water. At present, only the ratio of Hamaker constant between two oxides was obtained and compared with that obtained by other techniques. These oxides were ultrapure anatase TiO2 and γ-Al2O3, and they displayed a linear relationship between yield stress and the square of zeta potential. At the conductivity (or ionic strength) of about 3000 μS/cm, the critical zeta potential for both TiO2 and Al2O3 is ∼ 47 and ∼ 32 mV, respectively. These critical zeta potential data give a value of 2.2 for the ratio of Hamaker constant of anatase TiO2/H2O/TiO2 to γ-Al2O3/H2O/γ-Al2O3. This ratio compares well with a value ranging from 1.0 to 2.18 for rutile TiO2/H2O/TiO2 to α-Al2O3/H2O/α-Al2O3 where their Hamaker constants were calculated from the Lifshitz theory using full optical spectral data.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||dispersion; Hamaker Constant; rheology; yield stress; zeta potential|
|FoR Codes:||03 CHEMICAL SCIENCES > 0306 Physical Chemistry (incl Structural) > 030603 Colloid and Surface Chemistry @ 100%|
|SEO Codes:||86 MANUFACTURING > 8610 Ceramics, Glass and Industrial Mineral Products > 861099 Ceramics, Glass and Industrial Mineral Products not elsewhere classified @ 70%|
86 MANUFACTURING > 8615 Instrumentation > 861503 Scientific Instruments @ 30%
|Deposited On:||03 Mar 2010 08:54|
|Last Modified:||19 May 2013 00:59|
Last 12 Months: 0
|Citation Counts with External Providers:|
Repository Staff Only: item control page