Fatigue and deformation of HVOF sprayed WC-Co coatings and hard chrome plating
Ibrahim, A., and Berndt, C.C. (2007) Fatigue and deformation of HVOF sprayed WC-Co coatings and hard chrome plating. Materials Science and Engineering A: Structural Materials: Properties Microstructure and Processing, 456 (1-2). pp. 114-119.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://dx.doi.org/10.1016/j.msea.2006.12...
A challenge facing the finishing industry is to replace chrome plating since this technology has negative environmental and health effects. In the case of tungsten carbide and chrome carbide coatings, HVOF and detonation spray technologies have proven to be cleaner and more effective. In this paper, the results of a comparative investigation involve a detailed analysis of fatigue and deformation of two groups of AISI 4340 steel specimens. One group sprayed with HVOF WC–Co coating and the other group was plated with hard chrome. Rotating beam fatigue tests were performed on the coated and uncoated specimens. Optical and SEM microscopy were used to evaluate the fracture morphology. The fatigue life distributions of coated AISI 4340 steel specimens demonstrated that the HVOF coated specimens exhibited higher fatigue lives compared to the uncoated specimens.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||fatigue; WC-Co coating; fatigue life; hard chromium plating; HVOF; compressive resideual stress|
|FoR Codes:||09 ENGINEERING > 0914 Resources Engineering and Extractive Metallurgy > 091499 Resources Engineering and Extractive Metallurgy not elsewhere classified @ 100%|
|SEO Codes:||87 CONSTRUCTION > 8703 Construction Materials Performance and Processes > 870302 Metals (e.g. Composites, Coatings, Bonding) @ 100%|
|Deposited On:||21 Jul 2009 08:42|
|Last Modified:||24 May 2013 00:28|
Last 12 Months: 0
|Citation Counts with External Providers:||Web of Science: 20|
Repository Staff Only: item control page