Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 ceramics - a low temperature sintered material for LTCC applications
Jacob, Mohan V., Sudheendran, K., and Raju, K.C. James (2010) Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 ceramics - a low temperature sintered material for LTCC applications. Journal of the Australian Ceramic Society, 46 (2). pp. 54-58.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://www.austceram.com/ACS-Journal-201...
Ceramic samples with low sintering temperature were prepared by solid state reaction from the respective high purity oxide powders. Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7 were sintered below 900 degree Celcius and the density is above 90%. The frequency dependent dielectric properties of these ceramics up to 1MHz were measured using Agilent 4294A impedance analyser. The dielectric properties of Bi2 (Zn 2/3-x/3Nb4/3-2x/3Ti x)O7ceramics with x = 0 to 0.4 were estimated at microwave frequencies from room temperature to 15 K using Dielectric Post (DP) resonator techniques. The high dielectric permittivity together with the low sintering temperature will make this material an attractive candidate for LTCC applications.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||dielectric materials, dielectric constant, loss tangent, LTCC|
|FoR Codes:||09 ENGINEERING > 0912 Materials Engineering > 091201 Ceramics @ 100%|
|SEO Codes:||97 EXPANDING KNOWLEDGE > 970109 Expanding Knowledge in Engineering @ 100%|