Fabrication and characterisation of polymer thin-films derived from cineole using radio frequency plasma polymerisation
Easton, Christopher D., Jacob, Mohan V., and Shanks, Robert A. (2009) Fabrication and characterisation of polymer thin-films derived from cineole using radio frequency plasma polymerisation. Polymer, 50 (15). pp. 3465-3469.
|PDF (Published Version) - Repository staff only - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader|
View at Publisher Website: http://dx.doi.org/10.1016/j.polymer.2009...
The development of organic polymer thin-films is critical for the progress of many fields including organic electronics and biomedical coatings. This paper describes the fabrication of an organic polymer thin film produced from 1,8-cineole via radio frequency plasma polymerisation. A deposition rate of 55 nm/min was obtained under the polymerisation conditions employed. Infrared spectroscopic analysis demonstrated that some functional groups observed in the monomer were retained after the polymerisation process, while new functional groups were introduced. The refractive index and extinction coefficient were estimated to be 1.543 (at 500 nm) and 0.001 (at 500 nm) respectively. The polymers were shown to be optically transparent. AFM images of the polymer established a very smooth and uniform surface with average roughness of 0.39 nm. Water contact angle data demonstrated that the surface was stable while in contact with water.
|Item Type:||Article (Refereed Research - C1)|
|Keywords:||plasma polymerisation; 1,8-Cineole; thin-film|
|FoR Codes:||09 ENGINEERING > 0912 Materials Engineering > 091208 Organic Semiconductors @ 100%|
|SEO Codes:||97 EXPANDING KNOWLEDGE > 970109 Expanding Knowledge in Engineering @ 100%|
|Deposited On:||21 May 2010 14:23|
|Last Modified:||18 Oct 2013 01:03|
Last 12 Months: 0
|Citation Counts with External Providers:|
Repository Staff Only: item control page